AMERICAN ALUMINIUM ALLOYS


Round
Plate
Sheet
Flat
Square Bar
Hexagon
Angle
Tube
Profiles

 

American Aluminium Alloys
American Aluminium Alloys
American Aluminium Alloys

Nearest Equivalent Specification

Available Products

A high strength type 2024 alloy (3.8 to 4.9% copper) in extruded bar and profile form. Solution heat-treated and controlled stretched to achieve the T3511 condition.

2024 T3511
2024 T3510

AMS 4165
AMS 415

A medium strength type 6061 alloy. Solution treated, artificially aged and controlled stretched to achieve the T6511 condition, in extruded bar and profile form.

6061 T6511
6061 T6

AMS 4173
AMS 4150

A high strength type 7075 alloy (5.1 to 6.1% zinc). Solution treated, artificially aged and controlled stretched to achieve the T6511 condition, in extruded bar and profile form.

7075 T6511
7075 T6510

AMS 4169
AMS 4168

A high strength type 2024 alloy (3.8 to 4.9% copper). Available in drawn, rolled or cold finished form. Solution heat-treated and controlled stretched to achieve the T351 condition.

2024 T4
2024 T351

AMS 4120
AMS 4120

A medium strength type 6061 alloy. Solution treated, artificially aged and controlled stretched to achieve the T651 condition, in drawn, rolled or cold worked bar, profile and wire form.

6061 T6
6061 T651

AMS 4117
AMS 4117

A high strength type 7075 alloy (5.1 to 6.1% zinc). Solution treated, artificially aged and controlled stretched to achieve the T651 condition, in drawn, rolled, cold finished wire, bar and profile forms.

7075 T7351
7075 T651
7075 T6

AMS 4124
AMS 4123
AMS 4122

AMS QQ-A-250/4

Bare type 2024 alloy. Solution heat-treated, cold worked and naturally aged to achieve a substantially ‘T3’ condition.

2024 T3

AMS 4037

A high strength type 2024 alloy rolled sheet (3.8 to 4.9% copper). Alclad to 1.5% nominal material thickness.

2024 ’O’

AMS 4040

A medium strength type 6061 alloy solution treated and artificially aged to achieve the T6 condition. Also available in the ‘O’(annealed) and ‘T4’ (solution treated only) conditions to accommodate various degrees of forming, drawing or spinning.

6061 ‘O’
6061 T4
6061 T6

AMS 4025
AMS 4026
AMS 4027

AMS QQ-A-250/12

A high strength BARE type 7075 alloy. Solution heat treated and artificially aged to achieve the T6 condition. Also available in the ‘O’ condition for more severe, bending and forming operations.

7075 ‘O’
7075 T6

AMS 4044
AMS 4045

A high strength ALCLAD type 7075 alloy. Solution heat treated and artificially aged to achieve the T6 condition. Also available in the ‘O’ condition for more severe, bending and forming operations.

7075 ‘O’
7075 T6

AMS 4048
AMS 4049

AMS WW-T-700/3

A high strength type 2024 alloy (3.8 to 4.9% copper) in a drawn seamless tube form. Solution heat-treated, cold worked and naturally aged to achieve a substantially ‘T3’ condition. Also available as ‘O’(annealed) and ‘T4’ (solution treated only).

2024 ‘O’
2024 T3
2024 T4

AMS 4088
AMS 4088
AMS 4088

AMS WW-T-700/6

A medium strength type 6061 alloy solution treated and artificially aged to achieve the T6 condition. Also available in the ‘O’ (annealed) and ‘T4’ (solution treated only) conditions to accommodate various degrees of forming, drawing or spinning.

6061 ‘O’
6061 T4
6061 T6

AMS 4083
AMS 4083
AMS 4083